脱芯工艺对钴基高温合金DZ40M组织和性能的影响 |
||||||||||||||||||||
| 佟健, 陈甲祺, 郑志, 于永泗, 宁礼奎, 刘恩泽 | ||||||||||||||||||||
|
Effect of Leaching Process for Ceramic Core on Micro-structure and Mechanical Property of Investment Cast Co-base Superalloy DZ40M |
||||||||||||||||||||
| TONG Jian, CHEN Jiaqi, ZHENG Zhi, YU Yongsi, NING Likui, LIU Enze | ||||||||||||||||||||
| 表1 硅基脱芯工艺处理不同时间后样品的室温拉伸性能 | ||||||||||||||||||||
| Table 1 Tensile properties of DZ40M alloy immersed in Si-based core leaching medium for different times | ||||||||||||||||||||
|
||||||||||||||||||||