Zr-4合金在LiOH水溶液中腐蚀时氧化膜生长各向异性的研究*
苟少秋1,周邦新1,2(
),谢世敬1,徐龙1,2,姚美意1,李强1,2
),谢世敬1,徐龙1,2,姚美意1,李强1,2
INVESTIGATION OF THE ANISOTROPIC GROWTH OF OXIDE LAYERS FORMED ON Zr-4 ALLOYS CORRODED IN LiOH AQUEOUS SOLUTION
Shaoqiu GOU1,Bangxin ZHOU1,2(),Shijing XIE1,Long XU1,2,Meiyi YAO1,Qiang LI1,2
),Shijing XIE1,Long XU1,2,Meiyi YAO1,Qiang LI1,2
图5. 图4b中方框处c-ZrO2的(200)和(111)晶面的反Fourier变换图及应变分布图
Fig.5. IFFT patterns of (200) (a) and (111) (b) for c-ZrO2 area outlined in Fig.4b and strain fields obtained from the geometric phase images analyzed using Fig.5a (c) and Fig.5b (d) (Arrows in Figs.5a and b show the dislocation cores)