X65钢在含超临界CO2的NaCl溶液中腐蚀机制的讨论*
魏亮,庞晓露,高克玮(
)
)
CORROSION MECHANISM DISCUSSION OF X65 STEEL IN NaCl SOLUTION SATURATED WITH SUPERCRITICAL CO2
Liang WEI,Xiaolu PANG,Kewei GAO()
)
图11. X65钢在含有饱和SC CO2的NaCl水溶液中浸泡不同时间后的膜基界面富Cl-区的EDS分析和Cl-含量随浸泡时间的变化关系
Fig.11. EDS analyses (a) of the Cl--rich area at scale/matrix interface on X65 steel after immersed in NaCl solution saturated with SC CO2 for various time and the change of Cl- content with immersion time (b)