Al-Cr涂层的制备及抗热腐蚀性能研究

鲁金涛, 朱圣龙, 王福会

中国科学院金属研究所金属腐蚀与防护国家重点实验室, 沈阳 110016

Hot Corrosion Performance of Al-Cr Coatings Prepared by Pack Cementation

LU Jintao, ZHU Shenglong, WANG Fuhui

State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Science, Shenyang 110016

全文: PDF(1250 KB)

摘要: 采用粉末包埋法在Ni基高温合金K417G上制备Al-Cr涂层, 并研究其在25 NaCl+75 Na₂SO₄ (mass)盐膜下900℃的热腐蚀特性. 采用两步法沉积的Al-Cr涂层为双层结构, 外层为$\beta$-NiAl相和少量AlCr₂相, 平均Cr含量约为20 mass; 内层为互扩散带. 而采用一步法沉积的Al-Cr涂层具有三层结构, 外层和中间层均为β-NiAl相, 它们之间的主要差别是外层Cr含量为8 mass左右, 中间层Cr含量为3 mass左右, 内层也是互扩散带. 热腐蚀试验结果表明, 低Cr含量的Al-Cr涂层氧化膜易剥落, 抗热腐蚀性能较差; 高Cr含量的Al-Cr涂层表面能形成较完整的氧化膜, 抗热腐蚀性能明显优于低Cr含量的涂层.

关键词 ： Al-Cr涂层, 粉末包埋, 涂层结构, 热腐蚀

Abstract：Al-Cr coatings were prepared on Ni-based superalloy K417G by pack cementation method. Hot corrosion resistance of the coatings beneath deposits of 25 NaCl+75 Na₂SO₄ (mass) at 900℃ was investigated. The average Cr content of the formed two layered Al-Cr coating prepared by two step process was ca. 20 mass, of which the outer zone was com-posed of β-NiAl with a little AlCr₂ phase. In the contrast, a three layered coating was formed for the AlCr coating prepared by one step progress, of which Cr mainly existed in the outer zone (8 mass) and the middle zone (3 mass). The Al-Cr coating with high Cr content possessed much better resistance to hot corrosion at 900℃ beneath deposits of 25 NaCl+75 Na₂SO₄.

Key words： Al-Cr coating pack cementation coating microstructure hot corrosion

收稿日期: 2010-05-07

ZTFLH:

TG174.445

基金资助:

中国科学院创新工程项目(YYYJ-0912)资助

通讯作者: 鲁金涛 E-mail: jtlu@imr.ac.cn

Corresponding author: LU Jintao E-mail: jtlu@imr.ac.cn

作者简介: 鲁金涛 (1984-), 男, 博士生, 研究方向为高温涂层

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	鲁金涛
	朱圣龙
	王福会
44.8K

引用本文:

鲁金涛, 朱圣龙, 王福会. Al-Cr涂层的制备及抗热腐蚀性能研究[J]. 腐蚀科学与防护技术, 2011, 23(5): 399-402.
LV Jin-Shou, ZHU Ku-Long, YU Fu-Hui. Hot Corrosion Performance of Al-Cr Coatings Prepared by Pack Cementation. Cor Sci Pro Tech, 2011, 23(5): 399-402.

链接本文:

https://www.cspt.org.cn/CN/ 或 https://www.cspt.org.cn/CN/Y2011/V23/I5/399

[1] Godlewska E, Godlewski K. Chromaluminizing of nickel and its alloys[J]. Oxid. Met., 1984, 22(3-4): 117.

[2] 诸虎儿, 曹铁梁, 石声泰. 铬铝涂层及其抗高温腐蚀行为[J]. 中国腐蚀与防护学报, 1987, 7(2): 77.

[3] Bai C Y, Luo Y J. Improvement of high temperature oxidation and corrosion resistance of superalloy IN-738 by pack cementation[J]. Surf. Coat. Technol., 2004, 183(5): 74.

[4] 安涛峰, 孙晓峰, 管恒荣. 渗铝镍基高温合金热腐蚀行为研究[J].腐蚀科学与防护技术, 2000, 12(6): 323.

[5] Frederick D G, Robert A. R. Simultaneous chromizing-aluminizing coating of low-alloy steels by a halide-activated, pack-cementation process [J]. Oxid. Met., 1993,40(3-4): 213.

[6] Costa W D, Gleeson B, Young D J. Codeposited chromiun-aluminide coatings[J]. J. Electrochem. Soc., 1994, 141(6):1464.

[7] Xiang Z D, Datta P K. Conditons for codeposition of Al and Cr on nickel base superalloys by pack cementation process[J]. Surf.Eng., 2001, 17(4): 287.

[8] Robert B. The effect of NaCl on the mechanical behavior of protective scales at high temperatures[J]. J. Electrochem. Soc.,1989, 136(5): 265.

[9] 楼翰一. 几种镍基高温合金铬铝涂层的抗热腐蚀性能[J].中国腐蚀与防护学报, 1985, 5(4): 291.

[1]	刘丽, 于思荣. 稀土Y的添加对粉末包埋渗锌涂层耐腐蚀性能的影响[J]. 腐蚀科学与防护技术, 2018, 30(5): 475-480.
[2]	米丰毅,朱圣龙. 搪瓷涂层700 ℃长期抗高温氧化和热腐蚀行为研究[J]. 腐蚀科学与防护技术, 2015, 27(3): 254-258.
[3]	潘太军,李杰. 氯化物盐膜下Fe-Si合金加速腐蚀行为的研究[J]. 腐蚀科学与防护技术, 2014, 26(5): 401-406.
[4]	张毅斌,吴多利,张洪宇,韦华,郑启,金涛,孙晓峰. DZ40M合金表面4种渗层的热腐蚀性能[J]. 腐蚀科学与防护技术, 2014, 26(5): 483-486.
[5]	王勇;王文;辛丽;朱圣龙;王福会. 三种β-NiAl相材料的短期热腐蚀行为比较研究[J]. 腐蚀科学与防护技术, 2010, 22(1): 36-38.
[6]	张松; 张春华; 王明生; 王茂; 刘常升 . 耐热钢表面激光熔覆Co基合金涂层的高温性能[J]. 腐蚀科学与防护技术, 2008, 20(3): 181-183 .
[7]	于萍; 王亚权 . 稀土改性及渗铝处理对K38高温合金热腐蚀行为的影响[J]. 腐蚀科学与防护技术, 2008, 20(1): 5-7 .
[8]	王磊; 马颖澈; 高明; 赵秀娟; 刘奎 . NaCl沉积盐引起的1Cr25Ni20Si2合金在700℃～900℃的腐蚀行为研究[J]. 腐蚀科学与防护技术, 2007, 19(2): 87-91 .
[9]	付广艳; 刘群; 门冰洁; 蔡璐 . 机械合金化Ni-20Cr合金的热腐蚀行为[J]. 腐蚀科学与防护技术, 2006, 18(6): 396-399 .
[10]	李杰; 曾潮流 . (Na,K)2SO4沉积引起的纯Ni和M38G合金热腐蚀的电化学阻抗研究[J]. 腐蚀科学与防护技术, 2005, 17(1): 50-53 .
[11]	任鑫; 王福会; 汪信 . Al-Si涂层在900℃硫酸盐中的热腐蚀行为[J]. 腐蚀科学与防护技术, 2004, 16(4): 187-191 .
[12]	李凌峰; 沈嘉年; 李谋成; 武朋飞; 肖美群 . 不锈钢表面粉末包埋渗铝过程及渗铝层表征[J]. 腐蚀科学与防护技术, 2004, 16(2): 79-82 .
[13]	安涛峰; 孙晓峰; 管恒荣等 . 渗铝镍基高温合金热腐蚀行为研究[J]. 腐蚀科学与防护技术, 2000, 12(6): 323-325 .
[14]	何大雄; 管恒荣; 姜晓霞等 . Pd—Ni—Al涂层的循环氧化和在Na2SO4熔盐中的热腐蚀行为[J]. 腐蚀科学与防护技术, 2000, 12(4): 207-210 .
[15]	庞英;管恒荣;孙晓峰;姜晓霞. Pt-Al涂层在两种熔盐中的高温热腐蚀行为[J]. 腐蚀科学与防护技术, 1997, 9(1): 36-39.

Viewed

Full text

Abstract

Cited

Shared

Discussed