图5. Ti-3Al-8V-6Cr-4Mo-4Zr合金经800℃/30 min+500℃/12 h处理后拉伸试样中位错的形貌
Fig.5. TEM images of dislocation in the heat treatment conditions 800℃/30 min+500℃/12 h after tensile deformation