Preparation and Properties of Spherical Particles of Polymer Alloy Polypropylene/Polybutene-1 |
Hegang REN1(), Zhenyou LI2, Yibin YAN1, Sihan WANG1, Xiaopeng CUI3, Binyuan LIU3 |
1 Daqing Petrochemical Research Center, Petrochemical Research Institute of CNPC, Daqing 163714, China 2 Refining and Chemical Branch of CNPC, Beijing 100007, China 3 Institute of Polymer Science and Engineering, Hebei University of Technology, Tianjin 300130, China |
|
Cite this article:
Hegang REN, Zhenyou LI, Yibin YAN, Sihan WANG, Xiaopeng CUI, Binyuan LIU. Preparation and Properties of Spherical Particles of Polymer Alloy Polypropylene/Polybutene-1. Chinese Journal of Materials Research, 2018, 32(7): 518-524.
|
Abstract A new type of polymer alloy of polypropylene/polybutene-1 was prepared by in-situ polymerization with spherical Ziegler-Natta as catalyst. The effect of butene-1 addition on the morphology, structure and the properties of polymer alloy was investigated. The polymers obtained were characterized by means of DSC, SEM XRD and 13C NMR. The results show that compared with the bulk polymerization of butene-1, the in-situ polymerization could improve the morphology of the product made from polybutene-1, and effectively reduce the adhesion between polymer particles. The catalytic activity, stacking density and particle size of the prepared polymer alloy are 10.4 kg/gCat, 0.44 g/cm3 and 500 μm, respectively. Moreover, the in-situ polymerization could effectively shorten the transition period of the polybutene-1 product from the unstable crystal form II to the stable crystalline form I. The mechanical property test revealed that with the rise of the content of the structural unit in propylene the tensile strength and flexural modulus of the polybutene alloys were increased, however, the density, impact strength and elongation at break were decreased.
|
Received: 15 August 2017
|
|
[1] | Hua S S, Huang B C.Modification of small bulk polypropylene plant by 1-butene polymerization[J]. Sci. Technol. Innov. Herald, 2010, (24): 108(华树森, 黄宝琛. 小本体聚丙烯装置改造进行1-丁烯聚合[J]. 科技创新导报, 2010, (24): 108) | [2] | Huang B C, Zhang B Y, Yao W, et al.Bulk depositing synthesis process of isotactic polybutylene-1 [P]. Chin Pat, CN101020728A, 2007(黄宝琛, 郑保永, 姚薇等.高全同聚丁烯-1的本体沉淀合成方法 [P]. 中国专利,CN101020728A, 2007) | [3] | He A H, Wang C.Spherical polybutylene-1 with high isotacticity and preparation method thereof [P]. Chin Pat, CN103288993A, 2013(贺爱华, 王超. 高等规度球形聚丁烯-1及其制备方法 [P]. 中国专利, CN103288993A, 2013) | [4] | He A H, Zheng W P, Shi Y W, et al.In situ synthesis of polybutene-1/polypropylene spherical alloys within a reactor with an MgCl2-supported Ziegler-Natta catalyst[J]. Polym. Int ., 2012, 61: 1575 | [5] | Jiang B Y, Shao H F, He A H, et al.Sequential two-stage polymerization for synthesis of isotactic polypropylene/isotactic polybutene-1 alloys: composition, morphology and granule growing mechanism[J]. Polym. Chem ., 2015, 6: 3315 | [6] | Zhang X M, Bi F Y, Song W B, et al.Preparation method for high isotactic polybutene-1 [P]. Chin Pat, CN103772557A, 2014(张晓萌, 毕福勇, 宋文波等. 高等规聚丁烯-1的制备方法 [P]. 中国专利, CN103772557A, 2014) | [7] | Bi F Y, Song W B, Zhang X M, et al.Preparation of high isotactic polybutene-1[J]. Petrochem. Technol ., 2014, 43: 441(毕福勇, 宋文波, 张晓萌等. 高等规聚1-丁烯的制备[J]. 石油化工, 2014, 43: 441) | [8] | Liu B Y, Ren H G, Yang M, et al.Spherical catalyst for 1-butene polymerization as well as preparation method and application thereof [P]. Chin Pat, CN101914172B, 2012(刘宾元, 任合刚, 杨敏等.1-丁烯聚合用的球形催化剂及其制备方法和应用 [P]. 中国专利, CN101914172B, 2012) | [9] | Abedi S, Sharifi-Sanjani N.Preparation of high isotactic polybutene-1[J]. J. Appl. Polym. Sci ., 2000, 78: 2533 | [10] | Liu Y P, Cui K P, Tian N, et al.Stretch-induced crystal-crystal transition of polybutene-1: an in situ synchrotron radiation wide-angle X-ray scattering study[J]. Macromolecules, 2012, 45: 2764 | [11] | Resconi L, Camurati I, Malizia F.Metallocene catalysts for 1-butene polymerization[J]. Macromol. Chem. Phys ., 2006, 207: 2257 | [12] | Zhang C Y, Dong B, Zhang X Q, et al.Preparation and characterization of propylene/1-butene alloy with bulk copolymerization[J]. Chem. J. Chin. Univ ., 2014, 35: 2014(张春雨, 董博, 张学全等. 本体共聚合制备丙烯/1-丁烯合金及表征[J]. 高等学校化学学报, 2014, 35: 2014) | [13] | Ma Y P, Li L G, Shao H F, et al.Microstructure and its effect on the properties of poly(1-butene) alloys within reactor[J]. Chem. World, 2016, (5): 261(马亚萍, 李兰阁, 邵华锋等. 聚1-丁烯釜内合金的微观结构及其对性能的影响[J]. 化学世界, 2016, (5): 261) | [14] | Fisch M H, Dannenberg J J.Propylene incorporation in 1-butene copolymers by carbon-13 nuclear magnetic resonance spectrometry[J]. Anal. Chem ., 1977, 49: 1405 | [15] | Wang X F, Zhao Y X, Bi F Y, et al.The structure and properties of polybutene-1—(Ⅰ) the relation between isotacticity and properties of polybutene-1[J]. Polym. Mater. Sci. Eng ., 2008, 24(7): 66(王秀峰, 赵永仙, 毕福勇等. 全密度聚丁烯-1的结构与性能—(I)全同含量与聚丁烯-1性能的关系[J]. 高分子材料科学与工程, 2008, 24(7): 66) | [16] | Stolte I, Androsch R, Di Lorenzo M L, et al. Effect of aging the glass of isotactic polybutene-1 on form II nucleation and cold crystallization[J]. J. Phys. Chem. B, 2013, 117: 15196 | [17] | Li L, Liu T, Zhao L, et al.CO2-induced crystal phase transition from form II to I in isotactic poly-1-butene[J]. Macromolecules, 2009, 42: 2286 | [18] | Cecchin G, Marchetti E, Baruzzi G.On the mechanism of polypropene growth over MgCl2/TiCl4 catalyst systems[J]. Macromol. Chem. Phys ., 2001, 202: 1987 |
|